Loctite 3D 3172 Resin
LOCTITE 3D 3172 is engineered to produce functional parts requiring exceptional stiffness, superior surface finish, and outstanding impact resistance. It is ideal for fabricating components that may undergo machining, tapping, or polishing, ensuring longevity and mechanical characteristics comparable to polypropylene.
Biocompatibility: ISO 10993 -5/-23 passed
Key Mechanical Properties
- Tensile Stress at Break (MPa): 39
- Young’s Modulus (MPa): 1500
- Elongation at Break (%): 73
- IZOD Impact (Notched) (J/m): 52
- HDT at 0.455 MPa (°C): 100
Key Benefits
- Tough & Durable
- Superior Impact Strength
- Nice Surface Finish, Machinable
Ideal Applications
- Manufacturing Aids / Jigs & Fixtures
- Housings
- Insoles
Cleaning Process
LOCTITE 3D 3172 requires cleaning to achieve specified properties. Prior to post curing, support structures should be removed from the printed part, and the part should then be washed. Use compressed air to remove residual solvent from the surface of the material between intervals.
| Post Process Step | Agent | Method | Duration | Intervals | Additional Info |
|---|---|---|---|---|---|
| Cleaning | IPA | Ultrasonic | 2.5 min | 2 | Allow parts to dry between intervals |
| Dry | n.a. | Compressed air | 20 s | 2 | Air pressure (55psi) |
| Wait before post curing | n.a. | Ambient condition | 60 min | 1 | Room temperature |
Post Curing Process
LOCTITE 3D 3172 GY requires post curing to achieve specified properties. It is recommended that either an LED or wide spectrum lamp be used to post cure parts.
| UV Curing Unit | UV Source | Intensity | Cure Time per Side | Additional Settings |
|---|---|---|---|---|
| Loctite CL36 | 405nm LED | 80 mW/cm² at 405 nm | 20 min | 100% top & side, rotary table |
| Dymax 5000 EC Flood | Mercury Arc Bulb (broad spectrum) | 150 mW/cm² at 380 nm | 10 min | Shelf I |